China supplier aluminum oil cooler strip 5754
Basic Info
Model No.: 5754
Product Description
Specifications China supplier aluminum oil cooler strip 5754
Thickness: 0.3-6.0mm
Width: 10-1200mm
ISO9001: 2008,ISO14001:2004,MSDS,SGS
Chemical Composition
Characteristics This is a non-heat treatable alloy that is weldable. It is hardened by cold work. It has good forming characteristics and good corrosion resistance, including resistance to salt water. (1) Machinability
This alloy has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may (2) Forming
AL 5052 is readily formed at room temperature. Successive cold working decreases the formability. (3) Corrosion Resistance
Corrosion resistance to salt water and general atmospheric conditions is good. (4) Welding
This alloy is readily welded by conventional methods. When filler rod is required it should be aluminum alloy 5356 as filler. Either tungsten or consumable electrode inert gas shielded arc welding is preferred method. (5) Heat Treatment
AL 5052 cannot be hardened by means of heat treatment. It does harden due to cold working. (6) Forging
The alloy may be forged in the temperature range of 950 F down to 500 F. (7) Hot Working
Hot working, as with forging, may be done in the range of 950 F to 500 F. (8) Cold Working
The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary. (9) Annealing
Anneal at 650 F and air cool. (10) Hardening
Hardens only from cold working. (11) Other Physical Props
Electrical conductivity 33% of copper. (12) Other Mechanical Props
Shear strength for O temper is 18 ksi. For cold worked temper H 34 it is 21 ksi. Typical Application
Commonly used in the manufacture of hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, and appliances. Commonly used in sheet metal work and in sheet metal parts. Mechanical Properties
Contact us if you need more details on Aluminum 5754 H111. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Thin Aluminum Strip、Aluminum Floor Strips. If these products fail to match your need, please contact us and we would like to provide relevant information.
Thickness: 0.3-6.0mm
Width: 10-1200mm
ISO9001: 2008,ISO14001:2004,MSDS,SGS
Chemical Composition Cu | 0.10 |
Si+Fe | 0.45 |
Mn | 0.10 |
Mg | 2.2/2.8 |
Zn | 0.10 |
Cr | 0.15/0.35 |
Al | Balance |
This alloy has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may (2) Forming
AL 5052 is readily formed at room temperature. Successive cold working decreases the formability. (3) Corrosion Resistance
Corrosion resistance to salt water and general atmospheric conditions is good. (4) Welding
This alloy is readily welded by conventional methods. When filler rod is required it should be aluminum alloy 5356 as filler. Either tungsten or consumable electrode inert gas shielded arc welding is preferred method. (5) Heat Treatment
AL 5052 cannot be hardened by means of heat treatment. It does harden due to cold working. (6) Forging
The alloy may be forged in the temperature range of 950 F down to 500 F. (7) Hot Working
Hot working, as with forging, may be done in the range of 950 F to 500 F. (8) Cold Working
The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary. (9) Annealing
Anneal at 650 F and air cool. (10) Hardening
Hardens only from cold working. (11) Other Physical Props
Electrical conductivity 33% of copper. (12) Other Mechanical Props
Shear strength for O temper is 18 ksi. For cold worked temper H 34 it is 21 ksi. Typical Application
Commonly used in the manufacture of hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, and appliances. Commonly used in sheet metal work and in sheet metal parts. Mechanical Properties
Tensile Strength | 196-266MPa |
Yield Strength | 91-127MPa |
Elongation | 10-25 |
Brinell Hardness | 47-68 |
Product Categories : Aluminum Strip > 5000 Series Aluminum Strip
Premium Related Products
Other Products
Hot Products
aluminum sheet aa80116061 Temper O aluminum strip for bikeAluminum Coil 6063 used in buildingAluminum sheet 6082 T6 manufacturer1000 grade wide aluminum plate manufacturer5052 H26 aluminum alloy sheet good surface qualitygood quality cheap price 3003 temper H14/H24 aluminum strip Chinese manufacturerCold rolled anti-rust 3000 grade different width aluminum coil manufacturerBottle cover application 8011 in soft temper aluminum alloy coil cheap price good qualityCheap price aluminum band AA1050 H14 China manufacturerHigh-end application China market 5754 aluminum strip[Used for fan blade sheet ]good surface 1100 H18 1.2mm aluminum sheetGood quality mill finish 3004 H18 aluminum sheet China manufacturerDeep drawing material 8011 in soft temper O aluminum stripsMill finish surface 1100 H24 aluminum coil manufacturerTruck body application 5052 H32 aluminum sheet manufacturer